|Very low mass production cost||Tooling fees important (unsuitable for small quantities)|
|Reproducibility of aspherical lenses||More difficult to apply surface treatment|
|Weight (lighter than glass)||Less resistant to outside environment (UV, chemical, heat…)|
|Harder to break (more resistant than glass)||More easily skrachable (softer than glass)|
Two main material are used for optics in plastics : Polymethyl methacrylate (PMMA) or Polycarbonate (PC).
Also called “Acrylic glass”, PMMA is a transparent thermoplastic homopolymer known more commonly by the trade name “Plexiglas.” The material is similar to polycarbonate in that it is suitable for use as an impact resistant alternative to glass(particularly when the high impact strength of PC is not required).
It is generally considered one of the clearest plastics on the market.
PMMA is used for a variety of applications that typically take advantage of its natural transparency and the impact resistance
FOR OPTICAL USE :
Because of its clarity, it is also often used for windows or lenses. The raw material allows for the internal transmission of light nearly in the same capacity as glass which makes it a wonderful substitute.
PMMA is readily available and inexpensive which make a good material option for mass production of lenses.
Moreover, a major useful attribute about thermoplastics like PMMA is that they can be heated to their melting point, cooled, and reheated again without significant degradation. Instead of burning, thermoplastics like Acrylic liquefy, which allows them to be easily injection molded and then subsequently recycled.
|Technical Name||Poly(methyl methacrylate) -PMMA|
|Melt Temperature||130°C (266°F)|
|Thermal resistance||Very good (0.5×10-6 /K)|
|Typical Injection Mold Temperature||79-107°C (175-225°F)|
|Heat Deflection Temperature (HDT)||95°C (203°F) at 0.46 MPa (66 PSI)|
|Tensile Strength||65 MPa (9400 PSI)|
|Flexural Strength||90 MPa (13000 PSI)|
|Shrink Rate||0.2 – 1% (.002 – .01 in/in)|
PC is an amorphous thermoplastic with good transparent properties, but also available in many different colors. The choice for PC is usually made for product requiring transparency, impact resistance along with heat resistance.
Impact resistance comparatively with other commonly used plastic products:
FOR OPTICAL USE:
PC is commonly use for plastic optics through a molding process. Injection molding is a highly efficient method of reproducing optics with complex surface geometries. As a result, optics can be molded in varying volume requirements with a very high degree of part-to-part repeatability. However, due to high mold and set up costs this special process is only interesting for large quantities (usual minimum of 1000 parts).
Coating can also be applied such as AR, individual band pass or protection films.
|Technical Name||POLYCARBONATE (PC)|
|Melt Temperature||288-316 °C (550-600 °F)|
|Typical Injection Mold Temperature||82 – 121 °C (180 – 250 °F)|
|Heat Deflection Temperature (HDT)||140 °C (284 °F) at 0.46 MPa (66 PSI)|
|Tensile Strength||59 MPa (8500 PSI)|
|Flexural Strength||93 MPa (13500 PSI)|
|Shrink Rate||0.6 – 0.9 % (.006 – .009 in/in)|